Uniformity 6061 Paves the Way for Sintering Mass-Produced Aluminum Parts

Desktop Metal and Uniformity Labs have developed Uniformity 6061, a powder that enables aluminum sintering for binder jetting.

The new 6061 aluminum powder. (Image courtesy of Desktop Metal.)

The new 6061 aluminum powder. (Image courtesy of Desktop Metal.)

From a startup touting mysterious plug-and-play metal additive manufacturing (AM) technologies to going public on the New York Stock Exchange five years later, Desktop Metal is achieving its mission and taking AM to new levels. A multiyear collaboration with Uniformity Labs, an AM parts, printing and metal feedstock producer, has resulted in a new powder that enables sintering of unadulterated aluminum for binder jetting AM technology.

The new powder, Uniformity 6061, was the result of a combined goal to create a low-cost raw material option for dense, sinterable 6061 aluminum alloy parts. While 3D printing with aluminum may be nothing new, the options available have had their downsides. The majority of aluminum alloys available were for direct energy deposition, melting or direct metal laser sintering, which often came with a higher cost, limited build size, additional waste and finished parts with a rough surface. Creating an option for binder jetting enables larger build volumes, fewer geometry restrictions, faster printing and smoother surfaces.

“This breakthrough represents a major milestone in the development of aluminum for binder jetting and a significant step forward for the AM industry as it is one of the most sought-after materials for use in automotive, aerospace and consumer electronics,” said Ric Fulop, CEO and cofounder of Desktop Metal. “The global aluminum castings market is more than $50 billion per year, and it is ripe for disruption with binder jetting AM solutions.”

According to Desktop Metal, Uniformity 6061 has an elongation greater than 10 percent and provides both an improved yield strength and ultimate tensile strength when compared to wrought 6061 aluminum with similar heat treatments. The ability to use sintering means that powder particles don’t have to be coated, additional metals don’t have to be added and expensive nanoparticles aren’t required. The new powder is compatible with water-based binders and has a higher minimum ignition energy (MIE), giving it a safer profile.

“The introduction of lightweight metals to binder jetting opens the door to a wide variety of thermal and structural applications across industries,” said Adam Hopkins, founder and CEO of Uniformity Labs. “This innovation is a key step towards the adoption of mass-produced printed aluminum parts.”

Once available, the powder will be available for use on the Desktop Metal Production System. (Image courtesy of Desktop Metal.)

Once available, the powder will be available for use on the Desktop Metal Production System. (Image courtesy of Desktop Metal.)

During the next year, the companies will qualify the powder and scale its production. After it officially launches, Uniformity 6061will be suitable for use with Desktop Metal’s Production System 3D printer. This high-speed printer, which has an inert chemically inactive build chamber and auxiliary powder processing system, has a native 1200 x 1200 dpi resolution and layer heights as small as 50 µm, making it an ideal solution for taking aluminum 3D printing to the mass-market level.